Standard Test Method for Transverse Tensile Properties of Hoop Wound Polymer Matrix Composite Cylinders
Automaticky preložený názov:
Štandardná skúšobná metóda pre priečne mechanické vlastnosti Hoop rán Polymer Matrix Kompozitné fľaše
NORMA vydaná dňa 1.4.2012
Označenie normy: ASTM D5450/D5450M-12
Poznámka: NEPLATNÁ
Dátum vydania normy: 1.4.2012
Kód tovaru: NS-31244
Počet strán: 9
Približná hmotnosť: 27 g (0.06 libier)
Krajina: Americká technická norma
Kategória: Technické normy ASTM
Keywords:
composite materials, filament winding, Poisson´s ratio, transverse modulus of elasticity, transverse tensile properties, transverse tensile strength, tubes , Composites, Filament-wound materials, High modulus fibrous composites, Hoop wound polymer matrix composite cylinders, Poisson&apos,s ratio, Polymers, Tensile properties/testing--composites, Transverse modulus of elasticity, Transverse testing, Tubing, Wound polymer matrix composites, ICS Number Code 83.140.20 (Laminated sheets)
Significance and Use | ||||||||||||||||||||||||||||||||||||||
This test method is used to produce transverse tensile property data for material specifications, research and development, quality assurance, and structural design and analysis. Factors which influence the transverse tensile response and should, therefore, be reported are: material, methods of material preparation, specimen preparation, specimen conditioning, environment of testing, specimen alignment and gripping, speed of testing, void content, and fiber volume fraction. Properties, in the test direction, which may be obtained from this test method include: Transverse Tensile Strength, Transverse Tensile Strain at Failure, Transverse Tensile Modulus of Elasticity, E22, and Poisson's Ratio, υ21. |
||||||||||||||||||||||||||||||||||||||
1. Scope | ||||||||||||||||||||||||||||||||||||||
1.1 This test method determines the transverse tensile properties of wound polymer matrix composites reinforced by high-modulus continuous fibers. It describes testing of hoop wound (90°) cylinders in axial tension for determination of transverse tensile properties. 1.2 The technical content of this standard has been stable since 1993 without significant objection from its stakeholders. As there is limited technical support for the maintenance of this standard, changes since that date have been limited to items required to retain consistency with other ASTM D30 Committee standards, including editorial changes and incorporation of updated guidance on specimen preconditioning and environmental testing. The standard, therefore, should not be considered to include any significant changes in approach and practice since 1993. Future maintenance of the standard will only be in response to specific requests and performed only as technical support allows. 1.3 The values stated in either SI units or inch-pound units are to be regarded separately as standard. The values stated in each system are not exact equivalents; therefore, each system must be used independently of the other. Combining values from the two systems may result in nonconformance with the standard. 1.3.1 Within the text, the inch-pound units are shown in brackets. 1.4 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety and health practices and determine the applicability of regulatory limitations prior to use. |
||||||||||||||||||||||||||||||||||||||
2. Referenced Documents | ||||||||||||||||||||||||||||||||||||||
|
Historická
1.4.2010
Historická
1.11.2012
Historická
15.5.2014
Historická
15.7.2012
Historická
15.11.2011
Historická
1.12.2011
Posledná aktualizácia: 2024-11-22 (Počet položiek: 2 206 568)
© Copyright 2024 NORMSERVIS s.r.o.