ASTM F392/F392M-21
Standard Practice for Conditioning Flexible Barrier Materials for Flex Durability
NORMA vydaná dňa 1.5.2021
Informácie o norme:
Označenie normy: ASTM F392/F392M-21
Poznámka: NEPLATNÁ
Dátum vydania normy: 1.5.2021
Kód tovaru: NS-1053529
Počet strán: 3
Približná hmotnosť: 9 g (0.02 libier)
Krajina: Americká technická norma
Kategória: Technické normy ASTM
Kategórie - podobné normy:
Anotácia textu normy ASTM F392/F392M-21 :
Keywords:
barrier, barrier materials, flex crack, flex resistance, flexible, gas permeation, gas transmission rate, pinhole, water vapor transmission rate, WVTR,, ICS Number Code 55.040 (Packaging materials and accessories)
Doplňujúce informácie
| Significance and Use | ||||
|
5.1?This practice is valuable in determining the resistance of flexible packaging materials to flex-formed pinhole failures. Conditioning levels A, B, or C are typically used. Reference Practice E171 and Guide F2097. 5.2?Conditioning D and E are typically used for determining the effect of flexing on barrier properties transmission rates related to gas and/or moisture. 5.3?This practice does not measure or condition materials for abrasion related to flex failure. 5.4?Failures in the integrity of one or more of the plies of a multi-ply structure may require alternative testing. Supplementary permeation testing using gas or water vapor can be used in conjunction with the flex test to measure the loss of ply integrity. Other test methods may be used after flexing for assessment of presence of pinholes. For a list of test methods, refer to Guide F2097. FIG. 1 Planar Evolution of Gelbo Shaft Helical Groove 30.70-mm [1.20-in.] Diameter Shaft 5.4.1?The various conditions described in this practice are to prevent evaluating a material structure with an outcome of too many holes to effectively count (normally greater than 50), or too few to be significant (normally less than five per sample). Material structure, testing basis, and a mutual agreement with specified objectives are to be considered in the selection of conditioning level for testing. |
||||
| 1. Scope | ||||
|
1.1?This practice covers conditioning of flexible barrier materials for the determination of flex resistance. Subsequent testing can be performed to determine the effects of flexing on material properties. These tests are beyond the scope of this practice. 1.2?The values stated in either SI units or inch-pound units are to be regarded separately as standard. The values stated in each system may not be exact equivalents; therefore, each system shall be used independently of the other. Combining values from the two systems may result in non-conformance with the standard. 1.3?This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety, health, and environmental practices and determine the applicability of regulatory limitations prior to use. 1.4?This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee. |
||||
| 2. Referenced Documents | ||||
|
Odporúčame:
EviZak - všetky zákony vrátane ich evidencie na jednom mieste
Poskytovanie aktuálnych informácií o legislatívnych predpisoch vyhlásených v Zbierke zákonov od roku 1945.
Aktualizácia 2x v mesiaci !
Chcete vedieť viac informácii ? Pozrite sa na túto stránku.