Standard Practice for Making Reference Glass-Metal Butt Seals and Testing for Expansion Characteristics by Polarimetric Methods
Automaticky preložený názov:
Štandardná prax pre Making Referenčné sklo na kov Butt Tesnenie a testovanie pre expanziu Charakteristika polarimetrickou metódy
NORMA vydaná dňa 1.4.2008
Označenie normy: ASTM F140-98(2008)
Poznámka: NEPLATNÁ
Dátum vydania normy: 1.4.2008
Kód tovaru: NS-50159
Počet strán: 6
Približná hmotnosť: 18 g (0.04 libier)
Krajina: Americká technická norma
Kategória: Technické normy ASTM
Keywords:
expansion mismatch, glass-metal seals, Seals--electronic applications, Specimen preparation (for testing)--semiconductor materials, Thermal expansion/contraction, Butt seals, Electronic materials/applications, Glass electronic seals, Metal electronic components/devices, ICS Number Code 21.140 (Seals, glands)
Significance and Use | ||||||||
The term “reference” as employed in this practice implies that either the glass or the metal of the reference glass-metal seal will be a “standard reference material” such as those supplied for other physical tests by the National Institute for Standards and Technology (NIST), or a secondary reference material whose sealing characteristics have been determined by seals to a standard reference material. Until standard reference materials for seals are established by the NIST, secondary reference materials may be agreed upon between manufacturer and purchaser. |
||||||||
1. Scope | ||||||||
1.1 This practice covers the preparation and testing of reference glass-metal butt seals of two general configurations: one applicable to determining stress in the glass and the other to determining the degree of mismatch of thermal expansion (or contraction). Tests are in accordance with Test Method F 218 (Section 1.1). 1.2 This practice applies to all glass and metal (or alloy) combinations normally sealed together in the production of electronic components. It should not be attempted with glass-metal combinations having widely divergent thermal expansion (or contraction) properties. |
||||||||