Standard Reference Radiographs for Inspection of Aluminum and Magnesium Die Castings
Automaticky preložený názov:
Štandardný referenčný Röntgenové snímky pre inšpekciu hliníka a horčíka odliatky
NORMA vydaná dňa 1.8.2011
Označenie normy: ASTM E505-01(2011)
Poznámka: NEPLATNÁ
Dátum vydania normy: 1.8.2011
Kód tovaru: NS-47013
Počet strán: 3
Približná hmotnosť: 9 g (0.02 libier)
Krajina: Americká technická norma
Kategória: Technické normy ASTM
Keywords:
aluminum, die castings, discontinuities, magnesium, reference radiographs, X-ray: Aluminum alloys (castings), Die casting aluminum alloys, Die casting magnesium alloys, Magnesium alloy castings, Reference radiographs, ICS Number Code 77.040.20 (Non-destructive testing of metals)
Significance and Use | |||||||||||||||||||||||||||||||||||||||
These radiographs are so designed that acceptance standards, which may be developed for particular requirements, can be specified in terms of these radiographs. The radiographs are of castings that were produced under conditions designed to produce the discontinuities. These reference radiographs are intended to be used for casting thickness ranges in accordance with Table 1. The radiographic illustrations listed in Table 1 illustrate three types of discontinuities in four severity levels. Two ungraded illustrations have been included to establish the radiographic appearance of foreign material. These reference radiographs were produced in accordance with Guide E94. All of the references are original radiographs. Film Deterioration—Radiographic films are subject to wear and tear from handling and use. The extent to which the image deteriorates over time is a function of storage conditions, care in handling and amount of use. Reference radiograph films are no exception and may exhibit a loss in image quality over time. The radiographs should therefore be periodically examined for signs of wear and tear, including scratches, abrasions, stains, and so forth. Any reference radiographs which show signs of excessive wear and tear which could influence the interpretation and use of the radiographs should be replaced. TABLE 1 Reference Radiographs for Aluminum and Magnesium Die Castings
|
|||||||||||||||||||||||||||||||||||||||
1. Scope | |||||||||||||||||||||||||||||||||||||||
1.1 These reference radiographs illustrate the categories and severity levels of discontinuities that may occur in aluminum-alloy and magnesium-alloy die castings. They are intended to provide: 1.1.1 A guide enabling recognition of discontinuities and their differentiation both as to type and severity level through radiographic examination. 1.1.2 Example radiographic illustrations of discontinuities and a nomenclature for reference in acceptance standards, specifications, and drawings. 1.1.3 The values stated in inch-pound units are to be regarded as standard. The values given in parentheses are mathematical conversions to SI units that are provided for information only and are not considered standard. Note 1—The set of reference radiographs consists of five 8½ by 11-in. cardboard frames containing radiographs covering discontinuities in aluminum and magnesium alloy die castings. The first four frames each contain two sets of four graded levels of increasing severity, while the last frame contains two ungraded radiographs. The 5 frames are contained in a 10 ½ by 11½ -in. ring binder. Note 2—Reference radiographs applicable to aluminum and magnesium castings up to 2 in. (50 mm) in thickness are contained in ASTM Reference Radiographs E155, for Inspection of Aluminum and Magnesium Castings, Volumes I and II. 1.2 Two kinds of illustration categories are covered as follows: 1.2.1 Graded—Three discontinuity categories for aluminum die castings and three discontinuity categories for magnesium die castings, each illustrated in four levels of progressively increasing severity. Category A discontinuities are illustrated for aluminum and magnesium die castings having thicknesses of 1/8in. (3.2 mm) and 5/8 in. (15.9 mm); Category B discontinuities are illustrated for 1/8-in. thick aluminum and magnesium die castings; and Category C discontinuities are illustrated for 5/8-in. thick aluminum and magnesium die castings. 1.2.2 Ungraded—One illustration of one discontinuity for 0.20-in. (5.1-mm) thickness aluminum die casting; and one illustration of one discontinuity for 1/8-in. (3.2-mm) thickness magnesium die casting. 1.3 This document may be used for other materials, thicknesses, or with other energy levels for which it has been found to be applicable and agreement has been reached between the purchaser and manufacturer. 1.4 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety and health practices and determine the applicability of regulatory limitations prior to use. |
|||||||||||||||||||||||||||||||||||||||
2. Referenced Documents | |||||||||||||||||||||||||||||||||||||||
|
Chcete mať istotu, že používate len platné technické normy?
Ponúkame Vám riešenie, ktoré Vám zaistí mesačný prehľad o aktuálnosti noriem, ktoré používate.
Chcete vedieť viac informácií ? Pozrite sa na túto stránku.
Posledná aktualizácia: 2024-11-01 (Počet položiek: 2 208 817)
© Copyright 2024 NORMSERVIS s.r.o.