ASTM D7313-20
Standard Test Method for Determining Fracture Energy of Asphalt Mixtures Using the Disk-Shaped Compact Tension Geometry
NORMA vydaná dňa 15.12.2020
Informácie o norme:
Označenie normy: ASTM D7313-20
Dátum vydania normy: 15.12.2020
Kód tovaru: NS-1013169
Počet strán: 9
Približná hmotnosť: 27 g (0.06 libier)
Krajina: Americká technická norma
Kategória: Technické normy ASTM
Kategórie - podobné normy:
Anotácia textu normy ASTM D7313-20 :
Keywords:
asphalt concrete, crack growth, cracking, crack mouth opening displacement, disk-shaped compact tension test, fracture energy, temperature test,, ICS Number Code 93.080.20 (Road construction materials)
Doplňujúce informácie
| Significance and Use | ||||||||||||||||
|
4.1?The test method was developed for determining the fracture resistance of asphalt mixtures. The fracture resistance can help differentiate asphalt mixtures whose service life might be compromised by cracking. The test method is generally valid for specimens that are tested at temperatures of 10 ?C or below (see Note 1). The specimen geometry is readily adapted to 150 mm diameter specimens, such as fabricated from Superpave (trademark) gyratory compactors (Test Method D6925), which are used for the asphalt mixture design process. The specimen geometry can also be adapted for forensic investigations using field cores of pavements where thin lifts are present. This geometry has been found to produce satisfactory results for asphalt mixtures with nominal maximum aggregates size ranging from 4.75 to 19 mm (2). Note 1:?The stiffness of the asphalt binder tends to influence
the assessment of a valid test as described in 7.4. For instance, a soft asphalt binder
which may be required for a very cold climate might not lead to a
mixture that would produce valid results at +10 ?C and, conversely,
a hard asphalt binder utilized in hot climates may require higher
temperatures to provide any meaningful information.
Note 2:?The quality of the results produced by this test
method are dependent on the competence of the personnel performing
the procedure and the capability, calibration, and maintenance of
the equipment used. Agencies that meet the criteria of
Specification D3666 are
generally considered capable of competent and objective testing,
sampling, inspection, etc. Users of this test method are cautioned
that compliance with Specification D3666 alone does not completely ensure
reliable results. Reliable results may depend on many factors;
following the suggestions of Specification D3666 or some similar acceptable
guidelines provides a means of evaluating and controlling some of
those factors.
Note 3:?The failure mechanism experienced in this test is
influenced by the aggregate type due to the interactive effect of
asphalt binder stiffness and aggregate quality on the fracture path
and, therefore, fracture energy values. At high values of asphalt
binder stiffness, similar to those experienced near the
low-temperature performance grade of the asphalt binder, the crack
will travel around the aggregate when the mixture includes hard,
non-absorptive (for example, granite, trap rock) aggregates
resulting in a longer crack path and higher values of fracture
energy. For softer, more absorptive aggregates, the crack will
travel through the aggregate, shortening the crack path and leading
to lower values of fracture energy 1.1?This
test method covers the determination of fracture energy
(1.2?The
specimen geometry and terminology (disk-shaped compact tension,
DC(T)) is modeled after Test Method E399 for Plane-Strain Fracture Toughness
of Metallic Materials, Appendix A6, with modifications to allow
fracture testing of asphalt mix.
1.3?The test method describes the testing apparatus, instrumentation, specimen fabrication, and analysis procedures required to determine fracture energy of asphalt mixture and similar quasi-brittle materials. 1.4?The text of this test method references notes and footnotes which provide explanatory material. These notes and footnotes (excluding those in tables and figures) shall not be considered as requirements of the test method. 1.5?The values stated in SI units are to be regarded as the standard. No other units of measurement are included in this standard. 1.6?This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety, health, and environmental practices and determine the applicability of regulatory limitations prior to use. 1.7?This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee. |
||||||||||||||||
| 2. Referenced Documents | ||||||||||||||||
|
Odporúčame:
EviZak - všetky zákony vrátane ich evidencie na jednom mieste
Poskytovanie aktuálnych informácií o legislatívnych predpisoch vyhlásených v Zbierke zákonov od roku 1945.
Aktualizácia 2x v mesiaci !
Chcete vedieť viac informácii ? Pozrite sa na túto stránku.