Standard Test Method for Through-Thickness ""Flatwise"" Tensile Strength and Elastic Modulus of a Fiber-Reinforced Polymer Matrix Composite Material
Automaticky preložený názov:
Štandardná skúšobná metóda pre priechodná Hrúbka "naplocho", pevnosť v ťahu a modul pružnosti vystužených vláknami polymérnej matrice kompozitného materiálu
NORMA vydaná dňa 1.4.2007
Označenie normy: ASTM D7291/D7291M-07
Poznámka: NEPLATNÁ
Dátum vydania normy: 1.4.2007
Kód tovaru: NS-38088
Počet strán: 10
Približná hmotnosť: 30 g (0.07 libier)
Krajina: Americká technická norma
Kategória: Technické normy ASTM
Keywords:
composite materials, flatwise tension strength, interlaminar tensile strength, out-of-plane tension, through-thickness modulus of elasticity, through-thickness strength, ICS Number Code 83.120 (Reinforced plastics)
Significance and Use | ||||||||||||||||||||||||||||||||||||
This test method is designed to produce through-thickness failure data for structural design and analysis, quality assurance, and research and development. Factors that influence the through-thickness tensile strength, and should therefore be reported, include the following: material and fabric reinforcement, methods of material and fabric preparation, methods of processing and specimen fabrication, specimen stacking sequence, specimen conditioning, environment of testing, specimen alignment, speed of testing, time at temperature, void content, and volume reinforcement content. |
||||||||||||||||||||||||||||||||||||
1. Scope | ||||||||||||||||||||||||||||||||||||
1.1 This test method determines the through-thickness "flatwise" tension strength and elastic modulus of fiber reinforced polymer matrix composite materials. A tensile force is applied normal to the plane of the composite laminate using adhesively bonded thick metal end-tabs. The composite material forms are limited to continuous-fiber or discontinuous fiber (tape or 2-dimensional fabric, or both) reinforced composites. 1.2 The through-thickness strength results using this test method will in general not be comparable to Test Method D 6415 since this method subjects a relatively large volume of material to an almost uniform stress field while Test Method D 6415 subjects a small volume of material to a non-uniform stress field. 1.3 This standard does not purport to address all of the safety problems, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety and health practices and determine the applicability of regulatory limitations prior to use. 1.4 The values stated in either SI units or inch-pound units are to be regarded separately as standard. Within the text, the inch-pound units are shown in brackets. The values stated in each system are not exact equivalents; therefore, each system must be used independently of the other. Combining values from the two systems may result in nonconformance with the standard. |
||||||||||||||||||||||||||||||||||||