Standard Test Method for Rubber Properties´Measurement of Cure and After-Cure Dynamic Properties Using a Rotorless Shear Rheometer
NORMA vydaná dňa 1.5.2019
Označenie normy: ASTM D6601-19
Dátum vydania normy: 1.5.2019
Kód tovaru: NS-949125
Počet strán: 12
Približná hmotnosť: 36 g (0.08 libier)
Krajina: Americká technická norma
Kategória: Technické normy ASTM
Keywords:
dynamic properties, loss modulus, rotorless oscillating shear rheometer, storage modulus,, ICS Number Code 83.060 (Rubber)
Significance and Use | ||||||||
5.1 This test method is used to determine the vulcanization characteristics of (vulcanizable) rubber compounds under selected test conditions of strain and frequency which do not significantly affect the cured dynamic properties. In the same test, this test method also will measure the dynamic properties of the vulcanizate at temperatures significantly below the cure temperature. These lower temperature measurements are necessary in order to more effectively relate to rubber product service conditions. 5.2 This test method may be used for quality control in rubber manufacturing processes and for research and development testing of rubber compounds containing curatives. This test method also may be used for evaluating cure and dynamic property differences resulting from the use of different compounding ingredients. 5.3 For additional information regarding the significance of dynamic testing of vulcanized rubber, the reader may wish to reference Guide D5992. |
||||||||
1. Scope | ||||||||
1.1 This test method covers the use of a rotorless oscillating shear rheometer for measuring after cure dynamic properties at predetermined temperature(s) below the cure temperature. 1.2 Specified cure conditions that approximate a “static cure” also are covered to minimize effects on cured rubber compound dynamic properties. This test method is not intended to replace Test Method D5289. 1.3 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety, health, and environmental practices and determine the applicability of regulatory limitations prior to use. 1.4 Warning—Compounds based on silicone or fluoroelastomers may have high levels of thermal contraction or poor adhesion to the dies when cooled after the cure portion of this test method, causing slippage during strain sweeps. If this occurs, the results will not be reliable. 1.5 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee. |
||||||||
2. Referenced Documents | ||||||||
|
Poskytovanie aktuálnych informácií o legislatívnych predpisoch vyhlásených v Zbierke zákonov od roku 1945.
Aktualizácia 2x v mesiaci !
Chcete vedieť viac informácii ? Pozrite sa na túto stránku.
Posledná aktualizácia: 2024-11-21 (Počet položiek: 2 206 478)
© Copyright 2024 NORMSERVIS s.r.o.