Standard Test Method for Rubber Properties´Measurement of Cure and After-Cure Dynamic Properties Using a Rotorless Shear Rheometer
Automaticky preložený názov:
Štandardná skúšobná metóda pre Rubber Properties'Measurement Cure a After-Cure Dynamic Properties Použitie Rotorless nožnice Rheometer
NORMA vydaná dňa 1.12.2012
Označenie normy: ASTM D6601-12
Poznámka: NEPLATNÁ
Dátum vydania normy: 1.12.2012
Kód tovaru: NS-35829
Počet strán: 13
Približná hmotnosť: 39 g (0.09 libier)
Krajina: Americká technická norma
Kategória: Technické normy ASTM
Keywords:
dynamic properties, loss modulus, rotorless oscillating shear rheometer, storage modulus, ICS Number Code 83.060 (Rubber)
Significance and Use | ||||||||
5.1 This test method is used to determine the vulcanization characteristics of (vulcanizable) rubber compounds under selected test conditions of strain and frequency which do not significantly affect the cured dynamic properties. In the same test, this test method also will measure the dynamic properties of the vulcanizate at temperatures significantly below the cure temperature. These lower temperature measurements are necessary in order to more effectively relate to rubber product service conditions. 5.2 This test method may be used for quality control in rubber manufacturing processes and for research and development testing of rubber compounds containing curatives. This test method also may be used for evaluating cure and dynamic property differences resulting from the use of different compounding ingredients. 5.3 For additional information regarding the significance of dynamic testing of vulcanized rubber, the reader may wish to reference Guide D5992. |
||||||||
1. Scope | ||||||||
1.1 This test method covers the use of a rotorless oscillating shear rheometer for measuring after cure dynamic properties at predetermined temperature(s) below the cure temperature. 1.2 Specified cure conditions that approximate a “static cure” also are covered to minimize effects on cured rubber compound dynamic properties. This test method is not intended to replace Test Method D5289. 1.3 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety and health practices and determine the applicability of regulatory limitations prior to use. 1.4 Warning—Compounds based on silicone or fluoroelastomers may have high levels of thermal contraction or poor adhesion to the dies when cooled after the cure portion of this test method, causing slippage during strain sweeps. If this occurs, the results will not be reliable. |
||||||||
2. Referenced Documents | ||||||||
|
Chcete mať istotu, že používate len platné technické normy?
Ponúkame Vám riešenie, ktoré Vám zaistí mesačný prehľad o aktuálnosti noriem, ktoré používate.
Chcete vedieť viac informácií ? Pozrite sa na túto stránku.
Posledná aktualizácia: 2024-11-22 (Počet položiek: 2 206 568)
© Copyright 2024 NORMSERVIS s.r.o.