Standard Practice for Time-to-Failure (Creep-Rupture) of Adhesive Joints Fabricated from EPDM Roof Membrane Material
Automaticky preložený názov:
Štandardný postup doba do zlyhania (tečenie) z lepených spojov vyrobené z EPDM Strešný membránový materiál
NORMA vydaná dňa 1.12.2015
Označenie normy: ASTM D6383/D6383M-99(2015)
Poznámka: NEPLATNÁ
Dátum vydania normy: 1.12.2015
Kód tovaru: NS-622643
Počet strán: 3
Približná hmotnosť: 9 g (0.02 libier)
Krajina: Americká technická norma
Kategória: Technické normy ASTM
Keywords:
adhesive testing, creep, EPDM, joints, laboratory exposure, practice, roofing, seams, test conditions, time-to-failure,, ICS Number Code 91.060.20 (Roofs)
Significance and Use | ||||||||
5.1 An important factor affecting the performance of seams of EPDM membranes is their ability to remain bonded over the membrane's expected service life. Time-to-failure tests provide a means of characterizing the behavior of joints under constant load over time. Note 1: Table 1 is based
on the results of an industry government consortium study on
creep-rupture resistance (time-to-failure) of EPDM adhesive
joints.5.2 Time-to-failure tests complement
other mechanical tests such as strength for characterizing joints
of EPDM roof membranes, and can be incorporated in specifications
for adhesives for joining EPDM roof membrane material.
5.3 This practice, which is specific to EPDM joints, complements Test Method D5405 that provides general requirements for the preparation and creep-rupture testing of joints fabricated from any nonbituminous organic roof membrane material. 5.4 Laboratory experience in conducting time-to-failure tests of joints EPDM roof membranes has shown that specimens are less creep-resistant under peel loading than under shear loading. Consequently, the majority of the tests stipulated in this practice are performed under peel loading. 5.5 This practice does not develop time-to-failure data on all environmental conditions to which EPDM adhesive seams can be subjected in service. |
||||||||
1. Scope | ||||||||
1.1 This practice covers sample preparation temperatures, test parameters, and specimen exposure conditions that are applicable when Test Method D5405 is used for conducting time-to-failure (creep-rupture) tests of adhesive joints fabricated from ethylene-propylene-diene terpolymer (EPDM) roof membrane material. 1.2 This practice is applicable to joints fabricated in the laboratory from EPDM roof membrane materials and adhesives received from suppliers, and to joints prepared from EPDM seams sampled from field installations. 1.3 The joints are bonded using preformed tape or liquid-based adhesives, and EPDM roof membrane materials that are non-reinforced, fabric- or scrim-reinforced, and fabric backed. Primers are also used as recommended for the specific adhesive. 1.4 This practice contains notes that are explanatory and are not part of the mandatory requirements of this practice. 1.5 The values stated in either SI units or inch-pound units are to be regarded separately as standard. The values stated in each system may not be exact equivalents; therefore, each system shall be used independently of the other. Combining values from the two systems may result in non-conformance with the standard. 1.6 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety and health practices and determine the applicability of the regulatory limitations prior to use. |
||||||||