ASTM D6007-22

4.1?Upper limits for the formaldehyde emission rates have been established for wood panel building products made with urea-formaldehyde adhesives and permanently installed in homes or used as components in kitchen cabinets and similar industrial products. This test method is intended for use in conjunction with the test method referenced by HUD 24 for manufactured housing and by Minnesota Statutes for housing units and building materials. This method may also be used for monitoring products for compliance to the California Air Resources Board (CARB) regulation for composite wood products and the Environmental Protection Agency Formaldehyde Emission Standards for Composite Wood Products, EPA TSCA Title VI 40 CFR Section 770. This test method provides a means of testing smaller samples and reduces the time required for testing.

4.2?Formaldehyde concentration levels obtained by this small-scale method may differ from expected in full-scale indoor environments. Variations in product loading, temperature, relative humidity, and air exchange will affect formaldehyde emission rates and thus likely indoor air formaldehyde concentrations.

4.3?This test method requires the use of a chamber of 0.02 to 1 m³ in volume to evaluate the formaldehyde concentration in air using the following controlled conditions:

1.1?This test method measures the formaldehyde concentrations in air emitted by wood product test specimens under defined test conditions of temperature and relative humidity. Results obtained from this small-scale chamber test method are intended to be comparable to results obtained from testing larger product samples by the large chamber test method for wood products, Test Method E1333. The results may be correlated to values obtained from Test Method E1333. The quantity of formaldehyde in an air sample from the small chamber is determined by a modification of NIOSH 3500 chromotropic acid test procedure. As with Test Method E1333, other analytical procedures may be used to determine the quantity of formaldehyde in the air sample provided that such methods give results comparable to those obtained by using the chromotropic acid procedure. However, the test results and test report must be properly qualified and the analytical procedure employed must be accurately described.

1.2?The wood-based panel products to be tested by this test method are characteristically used for different applications and are tested at different relative amounts or loading ratios to reflect different applications. This is a test method that specifies testing at various loading ratios for different product types. However, the test results and test report must be properly qualified and must specify the make-up air flow, sample surface area, and chamber volume.

1.3?Ideal candidates for small-scale chamber testing are products relatively homogeneous in their formaldehyde release characteristics. Still, product inhomogeneities must be considered when selecting and preparing samples for small-scale chamber testing.

1.4?The values stated in SI units are to be regarded as standard. The values given in parentheses after SI units are provided for information only and are not considered standard.

1.5?This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety, health, and environmental practices and determine the applicability of regulatory limitations prior to use.

1.6?This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.