Standard Test Method for Water Absorption of Plastics (Includes all amendments And changes 8/8/2018).
Automaticky preložený názov:
Štandardná skúšobná metóda pre nasiakavosť plastov
NORMA vydaná dňa 1.4.2010
Označenie normy: ASTM D570-98(2010)e1
Poznámka: NEPLATNÁ
Dátum vydania normy: 1.4.2010
Kód tovaru: NS-32187
Počet strán: 4
Približná hmotnosť: 12 g (0.03 libier)
Krajina: Americká technická norma
Kategória: Technické normy ASTM
Keywords:
absorption, immersion, plastics, water, Immersion--plastics, Water analysis--plastics processing, ICS Number Code 83.120 (Reinforced plastics)
Significance and Use | ||
This test method for rate of water absorption has two chief functions: first, as a guide to the proportion of water absorbed by a material and consequently, in those cases where the relationships between moisture and electrical or mechanical properties, dimensions, or appearance have been determined, as a guide to the effects of exposure to water or humid conditions on such properties; and second, as a control test on the uniformity of a product. This second function is particularly applicable to sheet, rod, and tube arms when the test is made on the finished product. Comparison of water absorption values of various plastics can be made on the basis of values obtained in accordance with 7.1 and 7.4. Ideal diffusion of liquids into polymers is a function of the square root of immersion time. Time to saturation is strongly dependent on specimen thickness. For example, Table 1 shows the time to approximate time saturation for various thickness of nylon-6. The moisture content of a plastic is very intimately related to such properties as electrical insulation resistance, dielectric losses, mechanical strength, appearance, and dimensions. The effect upon these properties of change in moisture content due to water absorption depends largely on the type of exposure (by immersion in water or by exposure to high humidity), shape of the part, and inherent properties of the plastic. With nonhomogeneous materials, such as laminated forms, the rate of water absorption may be widely different through each edge and surface. Even for otherwise homogeneous materials, it may be slightly greater through cut edges than through molded surfaces. Consequently, attempts to correlate water absorption with the surface area must generally be limited to closely related materials and to similarly shaped specimens: For materials of widely varying density, relation between water-absorption values on a volume as well as a weight basis may need to be considered. |
||
1. Scope | ||
1.1 This test method covers the determination of the relative rate of absorption of water by plastics when immersed. This test method is intended to apply to the testing of all types of plastics, including cast, hot-molded, and cold-molded resinous products, and both homogeneous and laminated plastics in rod and tube form and in sheets 0.13 mm [0.005 in.] or greater in thickness. 1.2 The values given in SI units are to be regarded as standard. The values stated in brackets are for information only. 1.3 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety and health practices and determine the applicability of regulatory limitations prior to use. Note 1—ISO 62 is technically equivalent to this test method. |
||
2. Referenced Documents | ||
|
Historická
15.7.2013
Historická
15.7.2013
Historická
15.11.2012
Historická
1.4.2010
Historická
15.12.2012
Historická
1.10.2010
Posledná aktualizácia: 2024-11-22 (Počet položiek: 2 206 568)
© Copyright 2024 NORMSERVIS s.r.o.