ASTM D5272-08(2013)

4.1 When discarded as litter, articles made using photodegradable plastics are subject to attack by daylight (particularly solar-ultraviolet radiation), oxygen, heat, and water. The 5° exposure angle used in this practice represents typical conditions for degradation experienced by litter.

4.2 This practice requires characterization of the duration of exposure in terms of solar-ultraviolet radiation. Solar-ultraviolet radiation varies considerably as a function of location and time of year. This can cause dramatic differences in the time required to produce a specified level of degradation in a polymer. Daro⁴ has shown that when the same lot of polyethylene containing an iron-salt prodegradant is exposed at various times of the year in a single location, the time required to produce an average of two chain scissions per molecule varied by over 130 %. Daro, and Zerlaut and Anderson4.3 In addition to variations in level of daylight and solar-ultraviolet radiation, there are significant differences in temperature, and moisture stresses between different locations, and between different years, or periods within a single year, at a single location. Because of this variability, results from this test cannot be used to predict the absolute rate at which photodegradable plastics degrade. Results from this test can be used to compare relative rates of degradation for materials exposed at the same time in the same location. Results from multiple exposures of a common lot of material (during different seasons over several years) at different sites can be used to compare the relative rates at which a particular photodegradable plastic will degrade in each location.