ASTM D4255/D4255M-15
Standard Test Method for In-Plane Shear Properties of Polymer Matrix Composite Materials by the Rail Shear Method
Automaticky preložený názov:
Štandardná skúšobná metóda pre in - Plane šmyk polymérnej matrice kompozitných materiálov pri zábradlí šmyku Metóda
NORMA vydaná dňa 1.4.2015
Informácie o norme:
Označenie normy: ASTM D4255/D4255M-15
Poznámka: NEPLATNÁ
Dátum vydania normy: 1.4.2015
Kód tovaru: NS-588498
Počet strán: 13
Približná hmotnosť: 39 g (0.09 libier)
Krajina: Americká technická norma
Kategória: Technické normy ASTM
Anotácia textu normy ASTM D4255/D4255M-15 :
Keywords:
composite materials, shear modulus of elasticity, shear properties, shear strength,, ICS Number Code 83.140.20 (Laminated sheets)
Doplňujúce informácie
| Significance and Use | ||||||||||||||||||||||||||||||||||||||||||||
|
5.1 These shear tests are designed to produce in-plane shear property data for material specifications, research and development, and design. Factors that influence the shear response and should therefore be reported include: material, methods of material preparation and lay-up, specimen stacking sequence, specimen preparation, specimen conditioning, environment of testing, specimen alignment and gripping, speed of testing, time at temperature, void content, and fiber volume reinforcement content. Properties that may be measured by this test method include: 5.1.1 In-plane shear stress versus shear strain response, 5.1.2 In-plane shear chord modulus of elasticity, 5.1.3 Offset shear stress, and 5.1.4 Maximum in-plane shear stress. In cases in which the strain at failure is greater than 5 %, the shear stress corresponding to 5 % shear strain should be reported. |
||||||||||||||||||||||||||||||||||||||||||||
| 1. Scope | ||||||||||||||||||||||||||||||||||||||||||||
|
1.1 This test method determines the in-plane shear properties of high-modulus fiber-reinforced composite materials by either of two procedures. In Procedure A, laminates clamped between two pairs of loading rails are tested. When loaded in tension the rails introduce shear forces in the specimen. In Procedure B, laminates clamped on opposite edges with a tensile or compressive load applied to a third pair of rails in the center are tested. 1.2 Application of this test method is limited to continuous-fiber or discontinuous-fiber-reinforced polymer matrix composites in the following material forms: 1.2.1 Laminates composed only of unidirectional fibrous laminae, with the fiber direction oriented either parallel or perpendicular to the fixture rails. 1.2.2 Laminates composed only of woven fabric filamentary laminae with the warp direction oriented either parallel or perpendicular to the fixture rails. 1.2.3 Laminates of balanced and symmetric construction, with the 0° direction oriented either parallel or perpendicular to the fixture rails. 1.2.4 Short-fiber-reinforced composites with a majority of the fibers being randomly distributed. Note 1: Additional test methods for determining in-plane shear
properties of polymer matrix composites may be found in Test
Methods D5379/D5379M and
D5448/D5448M, and Practice
D3518/D3518M.
1.3 The values stated in either SI units or inch-pound units are to be regarded separately as standard. Within the text the inch-pounds units are shown in brackets. The values stated in each system are not exact equivalents; therefore, each system must be used independently of the other. Combining values from the two systems may result in nonconformance with the standard. 1.4 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety and health practices and determine the applicability of regulatory limitations prior to use. |
||||||||||||||||||||||||||||||||||||||||||||