ASTM D4060-07

Coating on substrates can be damaged by abrasion during manufacturing and service. This test method has been useful in evaluating the abrasion resistance of attached coatings. Ratings produced by this test method have correlated well with ratings produced by the falling abrasive values in Test Methods D 968.

For some materials, abrasion tests utilizing the Taber abraser may be subject to variation due to changes in the abrasive characteristics of the wheel during testing. Depending on abradant type and test specimen, the wheel surface may change (that is, become clogged) due to the pick-up of coating or other materials from test specimens and must be refaced at more frequent intervals as agreed upon by the interested parties. To determine if more frequent refacing is required, plot the total weight loss every 50 cycles. If a significant negative change in slope is observed prior to 500 cycles, the point at which the slope changes determines the refacing frequency.

1.1 This test method covers the determination of the resistance of organic coatings to abrasion produced by the Taber Abraser on coatings applied to a plane, rigid surface, such as a metal panel.

1.2 Because of the poor reproducibility of this test method, it should be restricted to testing in only one laboratory when numerical abrasion resistance values are to be used. Interlaboratory agreement is improved significantly when rankings of coatings are used in place of numerical values.

1.3 The values stated in SI units are to be regarded as the standard, with the exception of mils when determining coating thickness. The values given in parentheses are for information only.

1.4 This standard is similar in content (but not technically equivalent) to ISO 7784-2.

This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety and health practices and determine the applicability of regulatory limitations prior to use.