Standard Specification for Coal Fly Ash and Raw or Calcined Natural Pozzolan for Use in Concrete (Includes all amendments And changes 10/2/2015).
Automaticky preložený názov:
Štandardné špecifikácie pre uhlie popolčeka a Raw alebo kalcinovaný prírodný puzolán pre použitie v betóne
NORMA vydaná dňa 15.12.2012
Označenie normy: ASTM C618-12a
Poznámka: NEPLATNÁ
Dátum vydania normy: 15.12.2012
Kód tovaru: NS-14289
Počet strán: 5
Približná hmotnosť: 15 g (0.03 libier)
Krajina: Americká technická norma
Kategória: Technické normy ASTM
Keywords:
fly ash, natural pozzolan, pozzolans, ICS Number Code 91.100.30 (Concrete and concrete products)
1. Scope | |||
1.1 This specification covers coal fly ash and raw or calcined natural pozzolan for use in concrete where cementitious or pozzolanic action, or both, is desired, or where other properties normally attributed to fly ash or pozzolans may be desired, or where both objectives are to be achieved.
|
Class |
||
N |
F |
C |
|
Silicon dioxide (SiO2) plus aluminum oxide
(Al2O3) plus iron oxide
(Fe2O3), |
70.0 |
70.0 |
50.0 |
Sulfur trioxide (SO3), max, % |
4.0 |
5.0 |
5.0 |
Moisture content, max, % |
3.0 |
3.0 |
3.0 |
Loss on ignition, max, % |
10.0 |
6.0A |
6.0 |
Class
N
F
C
Fineness:
Amount retained when wet-sieved on 45 μm (No. 325) sieve, max, %
34
34
34
Strength activity index: A
With portland cement, at 7 days, min,
percent of
control
75B
75B
75B
With portland cement, at 28 days, min,
percent of
control
75B
75B
75B
Water requirement, max, percent of control
115
105
105
Soundness: C
Autoclave expansion or contraction, max, %
0.8
0.8
0.8
Uniformity requirements:
The density and fineness of individual
samples
shall not vary from the average established by the
ten preceding tests, or by all preceding tests if the
number is less than ten, by more than:
Density, max variation from average, %
5
5
5
Percent retained on 45-μm (No. 325), max
variation,
percentage points from average
5
5
5
Class
N
F
C
Increase of drying shrinkage of mortar
bars at 28 days, max, difference, in %,
over controlA
0.03
0.03
0.03
Uniformity Requirements:
In addition, when air-entraining
concrete is specified, the quantity of air-
entraining agent required to produce an air content of 18.0 vol %
of mortar
shall not vary from the average established by the ten preceding
tests or by all
preceding tests if less than ten, by more than, %
20
20
20
Effectiveness in Controlling Alkali-Silica Reaction:B
Expansion of test mixture as percentage
of low-alkali cement control, at 14
days, max, %
100
100
100
Effectiveness in Contributing to Sulfate Resistance:C
Procedure A:
Expansion of test mixture:
For moderate sulfate exposure after 6 months exposure, max, %
0.10
0.10
0.10
For high sulfate exposure after 6 months exposure, max, %
0.05
0.05
0.05
Procedure B:
Expansion of test mixture as a
percentage of sulfate resistance cement
control after at least 6 months exposure, max,%
100
100
100
1.3 The text of this standard references notes and footnotes, which provide explanatory information. These notes and footnotes (excluding those in tables and figures) shall not be considered as requirements of the standard.
Standard Test Methods for Sampling and Testing Fly Ash or Natural Pozzolans for Use in Portland-Cement Concrete |
|
Standard Terminology Relating to Concrete and Concrete Aggregates (Includes all amendments and changes 10/14/2021). |
Chcete mať istotu o platnosti využívaných predpisov?
Ponúkame Vám riešenie, aby ste mohli používať stále platné (aktuálne) legislatívne predpisy
Chcete vedieť viac informácií ? Pozrite sa na túto stránku.
Posledná aktualizácia: 2024-11-04 (Počet položiek: 2 209 323)
© Copyright 2024 NORMSERVIS s.r.o.