ASTM C156-09a
Standard Test Method for Water Loss [from a Mortar Specimen] Through Liquid Membrane-Forming Curing Compounds for Concrete (Includes all amendments And changes 6/22/2011).
Automaticky preložený názov:
Štandardná skúšobná metóda pre straty vody [ z malty Specimen ] až kvapalné membrány tvoriace vytvrdzovania zlúčeniny pre betón
NORMA vydaná dňa 15.12.2009
Informácie o norme:
Označenie normy: ASTM C156-09a
Poznámka: NEPLATNÁ
Dátum vydania normy: 15.12.2009
Kód tovaru: NS-11841
Počet strán: 5
Približná hmotnosť: 15 g (0.03 libier)
Krajina: Americká technická norma
Kategória: Technické normy ASTM
Anotácia textu normy ASTM C156-09a :
Keywords:
concrete curing materials, liquid membrane-forming curing compounds, moisture retention by concrete curing materials, Compound (curing), Curing (of concrete), Film, Liquid membrane-forming compounds, Sheet and film, Water retention, ICS Number Code 91.100.30 (Concrete and concrete products)
Doplňujúce informácie
| Significance and Use | ||||||||||||||||||
|
The moisture retaining ability of a product as determined by this test method is used to assess the suitability of materials for contributing to an appropriate curing environment for concrete. The laboratory test method is used both in formulating and in specifying or qualifying curing products. This test method gives the user a measure of the ability of tested curing materials to impede the escape of moisture from a hydraulic cement mortar. Since it is desirable to retain moisture in fresh concrete to promote the hydration process, failure of the product to minimize the escape of moisture may lead to loss of strength, cracking, shrinkage, or low abrasion resistance of the hardened concrete, or a combination thereof. Many factors affect the laboratory test results. Test results obtained may be highly variable as indicated by the precision statement. Critical factors include the precision of the control of the temperature, humidity and air circulation in the curing cabinet, preparation and sealing of the mortar specimens, the age and surface condition of the mortar specimen when the curing product is applied, and the uniformity and quantity of application of the curing membrane. |
||||||||||||||||||
| 1. Scope | ||||||||||||||||||
|
1.1 This test method covers laboratory determination of the efficiency of liquid membrane-forming compounds for curing concrete, as measured by their ability to reduce moisture loss during the early hardening period. 1.2 The values stated in SI units are to be regarded as standard. The values given in parentheses are mathematical conversions to inch-pound units that are provided for information only and are not considered standard. 1.3 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety and health practices and determine the applicability of regulatory limitations prior to use.(Warning—Fresh hydraulic cementitious mixtures are caustic and may cause chemical burns to skin and tissue upon prolonged exposure.) |
||||||||||||||||||