ASTM B947-06(2013)
Standard Practice for Hot Rolling Mill Solution Heat Treatment for Aluminum Alloy Plate
Automaticky preložený názov:
Štandardná prax pre Hot Rolling Mill homogenizácii pre hliníkové zliatiny Plate
NORMA vydaná dňa 1.5.2013
Informácie o norme:
Označenie normy: ASTM B947-06(2013)
Poznámka: NEPLATNÁ
Dátum vydania normy: 1.5.2013
Kód tovaru: NS-8888
Počet strán: 4
Približná hmotnosť: 12 g (0.03 libier)
Krajina: Americká technická norma
Kategória: Technické normy ASTM
Anotácia textu normy ASTM B947-06(2013) :
Keywords:
aluminum alloys, hot rolling, hot rolling mill solution heat treatment, slab, solution heat treatment, ICS Number Code 77.150.10 (Aluminium products)
Doplňujúce informácie
| 1. Scope | |
|
1.1 This practice establishes the controls required for hot rolling mill solution heat treatment of the 6xxx series aluminum alloy plate in Table 1 when ASTM material specifications allow use of this process in lieu of furnace solution heat treatment. For the alloys listed in Table 1, this practice is an alternate process to solution heat treatment in a furnace, such as specified in Practice B918 as the preliminary step for the attainment of T651-type tempers (see ANSI H35.1). Alloy |
Ingot Upper Limit Temperature |
|
6061 |
1050 [565] |
1.2 This practice applies only to
hot rolling mill solution heat treatment of plate for the listed
aluminum alloys. Precipitation hardening (aging) processing and
equipment calibration for aging shall meet the practice and
requirements of Practice B918.
1.3 The values stated in either SI units or inch-pound units are to be regarded separately as standard. The values stated in each system may not be exact equivalents; therefore, each system shall be used independently of the other. Combining values from the two systems may result in nonconformance with the standard.
1.4 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety and health practices and determine the applicability of regulatory limitations prior to use.
|
ASTM MNL7 |
Manual on Presentation of Data and Control Chart Analysis |
|
Standard Specification for Aluminum and Aluminum-Alloy Sheet and Plate (Metric) (Withdrawn 2021) |
|
|
Standard Terminology Relating to Aluminum- and Magnesium-Alloy Products |
|
|
Standard Test Methods for Tension Testing Wrought and Cast Aluminum- and Magnesium-Alloy Products |
|
|
EN 485-2 |
Aluminium and Aluminium Alloys--Sheet, Strip And Plate--Part 2: Mechanical Properties Available from European Committee for Standardization (CEN), 36 rue de Stassart, B-1050, Brussels, Belgium. |
|
H35.1/H35.1M |
Alloy and Temper Designation Systems for Aluminum Available from the Aluminum Association, Inc., 1525 Wilson Blvd. Suite 600, Arlington, VA 22209, www.aluminum.org. |
|
Standard Practice for Process Capability and Performance Measurement |
|
|
Standard Specification for Aluminum and Aluminum-Alloy Sheet and Plate |
|
|
Standard Test Methods for Tension Testing Wrought and Cast Aluminum- and Magnesium-Alloy Products (Metric) |
|
|
Standard Practice for Heat Treatment of Wrought Aluminum Alloys |
Odporúčame:
EviZak - všetky zákony vrátane ich evidencie na jednom mieste
Poskytovanie aktuálnych informácií o legislatívnych predpisoch vyhlásených v Zbierke zákonov od roku 1945.
Aktualizácia 2x v mesiaci !
Chcete vedieť viac informácii ? Pozrite sa na túto stránku.