Standard Specification for Nickel-Chromium-Molybdenum-Columbium Alloy (UNS N06625), Nickel-Chromium-Molybdenum-Silicon Alloy (UNS N06219), and Nickel-Chromium-Molybdenum-Tungsten Alloy (UNS N06650) Rod and Bar
Automaticky preložený názov:
Štandardné špecifikácie pre nikel-chróm-molybdénovej-niób zliatiny (UNS N06625), nikel-chróm-molybdénovej-kremík (UNS N06219), a nikel-chróm-molybdénovej-Tungsten Alloy (UNS N06650) tyč
NORMA vydaná dňa 1.10.2014
Označenie normy: ASTM B446-03(2014)
Poznámka: NEPLATNÁ
Dátum vydania normy: 1.10.2014
Kód tovaru: NS-6726
Počet strán: 5
Približná hmotnosť: 15 g (0.03 libier)
Krajina: Americká technická norma
Kategória: Technické normy ASTM
Keywords:
bar, rod, UNS N06625, UNS N06219, UNS N06650, ICS Number Code 77.150.40 (Nickel and chromium products)
1. Scope | ||||||||||
1.1 This specification covers nickel-chromium-molybdenum-columbium (UNS N06625), nickel-chromium-molybdenum-silicon alloy (UNS N06219), and Nickel-Chromium-Molybdenum-Tungsten Alloy (UNS N06650)2 in the form of hot-worked rod and bar and cold-worked rod in the conditions shown in Table 1. † MPa was corrected editorially.
1.1.1 UNS N06625 products are furnished in two grades of different heat-treated conditions: 1.1.1.1 Grade 1 (Annealed)—Material is normally employed in service temperatures up to 1100°F (593°C). 1.1.1.2 Grade 2 (Solution Annealed)—Material is normally employed in service temperatures above 1100°F (593°C) when resistance to creep and rupture is required. Note 1: Hot-working or reannealing may change properties
significantly, depending on working history and
temperatures.
1.1.2 Alloys UNS N06219 and UNS N06650 are supplied in solution annealed condition only. 1.2 The values stated in inch-pound units are to be regarded as standard. The values given in parentheses are mathematical conversions to SI units that are provided for information only and are not considered standard. 1.3 The following precautionary caveat pertains only
to the test methods portion, Section 12, of this specification:
Standard Specification for
Nickel-Chromium-Molybdenum-Columbium Alloy and
Nickel-Chromium-Molybdenum-Silicon Alloy Plate, Sheet, and
Strip Standard Test Methods for Chemical
Analysis of Nickel, Cobalt, and High-Temperature Alloys Standard Practice for Using Significant
Digits in Test Data to Determine Conformance with
Specifications Standard Test Methods for Tension Testing
of Metallic Materials Standard Specification for General
Requirements for Chemical Check Analysis Limits for Nickel, Nickel
Alloys and Cobalt Alloys |