Standard Test Method for Measurement of Stain Resistance of Anodic Coatings on Aluminum
NORMA vydaná dňa 1.5.2023
Označenie normy: ASTM B136-23
Dátum vydania normy: 1.5.2023
Kód tovaru: NS-1143467
Počet strán: 3
Približná hmotnosť: 9 g (0.02 libier)
Krajina: Americká technická norma
Kategória: Technické normy ASTM
This specification covers measurement of strain resistance of anodic coatings on aluminium and its alloys, that have undergone a sealing treatment and contact with an acidic solution, are stainproof or nonadsorptive with respect to dyes. The method comprises contacting the test area of the anodized specimen with nitric acid solution and, after rinsing and drying, applying a special dye solution followed by rinsing and rubbing the test area with pumice powder, drying, and visual examination of the test area for retention of dye stain. Coatings that exhibit no dye stain or change in color are considered to have passed the test. Reagent grade chemicals shall be used in all tests. A specified solution of nitric acid shall be prepared in distilled or deionized water. A specified volume of aluminium blue 2WL dye shall be dissolved in distilled or deionized water.
Keywords:
aluminum, sealing, stain,, ICS Number Code 25.220.20 (Surface treatment)
Significance and Use |
3.1?This test method is intended to determine whether anodic oxide coatings on aluminum and its alloys have been properly sealed and as a result are resistant to absorbing dyes. |
1. Scope |
1.1?This test method is intended to determine whether anodic oxide coatings on aluminum and its alloys, that have undergone a sealing treatment and contact with an acid solution, are stainproof or nonadsorptive with respect to dyes. 1.2?Coatings that have been properly sealed should be proof against adsorption of coloring materials and, hence, nonstaining in many types of service. 1.3?This test method is applicable to anodic coatings intended for applications where they are exposed to the weather, or for protective purposes in corrosive media, and where resistance to staining is important. Note 1:?Performance in this test is predictive only of
susceptibility to stain by dyes. It is not intended to be
predictive of other factors in service performance such as pitting
or general corrosion.
Note 2:?For Aluminum Association Class I and II architectural
anodic coatings that are sealed in solutions containing less than
15 ppm silicates or 3 ppm phosphates, the acid pretreatment may be
omitted.
1.4?In the case of coatings colored in deep shades, where estimation of the intensity of any residual dye stain is difficult, interpretation of the test is based on whether or not the original color has been affected by the action of the test. 1.5?This test method is not applicable to: 1.5.1?Chromic acid type anodic coatings. 1.5.2?Anodic coatings on aluminum alloys containing more than 2 mass % Cu or 4.5 mass % Si. 1.5.3?Anodic coatings that have been sealed only in dichromate solutions. 1.5.4?Anodic coatings that have undergone a treatment to render them hydrophobic. 1.6?The values stated in SI units are to be regarded as standard. No other units of measurement are included in this standard. 1.7?This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety, health, and environmental practices and determine the applicability of regulatory limitations prior to use. 1.8?This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee. |