Standard Specification for High-Strength Low-Alloy Steel Shapes of Structural Quality, Produced by Quenching and Self-Tempering Process (QST)
NORMA vydaná dňa 1.9.2019
Označenie normy: ASTM A913/A913M-19
Dátum vydania normy: 1.9.2019
Kód tovaru: NS-970173
Počet strán: 4
Približná hmotnosť: 12 g (0.03 libier)
Krajina: Americká technická norma
Kategória: Technické normy ASTM
This guide covers high-strength low-alloy steel shapes of structural quality, produced by quenching and self-tempering process (QST). The chemical analysis of the heat and of the steel product analysis shall conform to the chemical requirements prescribed by the reference materials. The Charpy V-notch test shall be performed to determine if the material conforms to the required tensile properties.
Keywords:
high-strength low-alloy steel, QST, quenching and self-tempering process, steel shapes, structural shapes, structural steel,, ICS Number Code 77.140.70 (Steel profiles)
1. Scope | ||||||
1.1 This specification covers high-strength low-alloy structural steel shapes in Grades 50 [345], 60 [415], 65 [450], 70 [485], and 80 [550], produced by the quenching and self-tempering process (QST). The shapes are intended for riveted, bolted or welded construction of bridges, buildings and other structures. 1.2 The QST process consists of in line heat treatment and cooling rate controls which result in mechanical properties in the finished condition that are equivalent to those attained using heat treating processes which entail reheating after rolling. A description of the QST process is given in Appendix X1. 1.3 Due to the inherent characteristics of the QST process, Grade 50 [345], 60 [415], 65 [450], and 70 [485] shapes shall not be formed nor post weld heat treated at temperatures exceeding 1100°F [595°C] and Grade 80 [550] shapes shall not be formed nor post weld heat treated at temperatures exceeding 1000°F [540°C]. 1.4 When the steel is to be welded, it is presupposed that a welding procedure suitable for the grade of steel and intended use or service will be utilized. See Appendix X3 of Specification A6/A6M for information on weldability. 1.5 The values stated in either inch-pound units or SI units are to be regarded separately as standard. Within the text, the SI units are shown in brackets. The values stated in each system are not exact equivalents; therefore, each system must be used independently of the other. Combining values from the two systems may result in nonconformance with this specification. 1.6 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee. |
||||||
2. Referenced Documents | ||||||
|
Poskytovanie aktuálnych informácií o legislatívnych predpisoch vyhlásených v Zbierke zákonov od roku 1945.
Aktualizácia 2x v mesiaci !
Chcete vedieť viac informácii ? Pozrite sa na túto stránku.
Posledná aktualizácia: 2024-09-08 (Počet položiek: 2 346 102)
© Copyright 2024 NORMSERVIS s.r.o.