Standard Specification for Free-Machining Ferritic Stainless Soft Magnetic Alloy Bar for Relay Applications
NORMA vydaná dňa 1.10.2018
Označenie normy: ASTM A838-18
Dátum vydania normy: 1.10.2018
Kód tovaru: NS-902027
Počet strán: 4
Približná hmotnosť: 12 g (0.03 libier)
Krajina: Americká technická norma
Kategória: Technické normy ASTM
This specification covers free-machining ferritic stainless soft magnetic alloy produced or supplied expressly in cold-finished bar form for use in magnetic cores and other parts requiring a high permeability, low-coercivity stainless steel. Two specific alloy types are covered: Grades, alloy type 1 and Grades, alloy type 2. The material shall conform to the chemical composition requirements specified. Material shall be tested using either ring, permeameter, or coercimeter test methods to meet the required specifications.
Keywords:
coercive field strength, coercivity, ferritic stainless steel, free-machining, relay,, ICS Number Code 77.140.40 (Steels with special magnetic properties)
1. Scope | ||||||||||||||||
1.1 This specification covers free-machining ferritic stainless soft magnetic alloy produced or supplied expressly in cold-finished bar form for use in magnetic cores and other parts requiring a high permeability, low-coercivity stainless steel. 1.1.1 This specification does not cover either cast parts or parts produced by powder metallurgy techniques. 1.2 Two specific alloy types are covered. The primary constituents are shown in Table 1. These types have corrosion resistance similar to AISI Type 430F and Type 430F, Specification A582/A582M. 1.3 This specification covers only these alloy types supplied in cold-finished bars in cross-sectional shapes such as rounds, squares, hexagons, and octagons with diameters (diagonals) greater than or equal to 6.35 mm (0.250 in.) and less than or equal to 41.5 mm (1.63 in.).2 1.4 Certain cold-finished round bar products are capable of being supplied mill annealed to required magnetic properties such as low coercivity. The size range that can be mill annealed is from 6.35 to 41.5 mm (0.250 to 1.63 in.). Other products of these alloys cannot be mill annealed to produce equivalently low coercivity; hence, the final machined parts should be heat treated as recommended by the producer. 1.5 The values stated in SI units are to be regarded as standard. The values given in parentheses are mathematical conversions to customary (cgs-emu and inch-pound) units which are provided for information only and are not considered standard. 1.6 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety, health, and environmental practices and determine the applicability of regulatory limitations prior to use. 1.7 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee. |
||||||||||||||||
2. Referenced Documents | ||||||||||||||||
|
Chcete mať istotu, že používate len platné technické normy?
Ponúkame Vám riešenie, ktoré Vám zaistí mesačný prehľad o aktuálnosti noriem, ktoré používate.
Chcete vedieť viac informácií ? Pozrite sa na túto stránku.
Posledná aktualizácia: 2024-05-03 (Počet položiek: 2 896 946)
© Copyright 2024 NORMSERVIS s.r.o.