ASTM A693-22
Standard Specification for Precipitation-Hardening Stainless and Heat-Resisting Steel Plate, Sheet, and Strip
NORMA vydaná dňa 1.9.2022
Informácie o norme:
Označenie normy: ASTM A693-22
Dátum vydania normy: 1.9.2022
Kód tovaru: NS-1086039
Počet strán: 8
Približná hmotnosť: 24 g (0.05 libier)
Krajina: Americká technická norma
Kategória: Technické normy ASTM
Kategórie - podobné normy:
Anotácia textu normy ASTM A693-22 :
This guide covers standard specification for precipitation-hardening stainless steel plate, sheet, and strip. The mechanical properties of these steels shall be developed by suitable low-temperature heat treatments or precipitation hardening. The steel shall conform to the required chemical composition for carbon, manganese, phosphorus, sulfur, silicon, chromium, nickel, aluminum, molybdenum, titanium, copper, and other elements. Material of types other than Type UNS S46910 shall be furnished in solution-annealed condition while Type UNS S46910 shall be furnished in cold-worked condition. The steel shall conform to the required mechanical properties such as tensile strength, yield strength, elongation, and hardness. Samples cut from the solution-annealed plate, sheet, or strip shall withstand cold bending without cracking on the outside of the bent portion. Samples cut from the solution-annealed plate, sheet, or strip shall conform to the specified mechanical properties when precipitation hardened.
Keywords:
plate, precipitation hardening, sheet, stainless steel, strip,, ICS Number Code 77.140.20 (Steels of high quality),77.140.50 (Flat steel products and semi-products)
Doplňujúce informácie
| 1. Scope | ||||||
|
1.1?This specification1.2?These steels are used for parts requiring corrosion resistance and high strength at room temperature or at temperatures up to 600 ?F (315 ?C). Some of these steels are particularly suitable for moderate to severe drawing and forming in the solution-treated condition. Others are capable of mild forming only. They are suitable for machining in the solution-annealed condition, after which they may be hardened to the mechanical properties specified in this standard without danger of cracking or distortion. 1.3?The values stated in inch-pound units are to be regarded as the standard. 1.4?This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee. |
||||||