ASTM A536-84(2019)e1
Standard Specification for Ductile Iron Castings (Includes all amendments and changes 5/3/2019).
NORMA vydaná dňa 1.5.2019
Informácie o norme:
Označenie normy: ASTM A536-84(2019)e1
Dátum vydania normy: 1.5.2019
Kód tovaru: NS-948444
Počet strán: 6
Približná hmotnosť: 18 g (0.04 libier)
Krajina: Americká technická norma
Kategória: Technické normy ASTM
Kategórie - podobné normy:
Anotácia textu normy ASTM A536-84(2019)e1 :
This specification covers ductile iron castings, also known as spheroidal or nodular iron, that is described as cast iron with the graphite substantially spheroidal in shape and essentially free of other forms of graphite. Appropriate heat treatment shall be identified according to grades, as follows: a full ferritizing anneal for 60-40-18; a quench and temper, or normalize and temper, or isothermal heat treatment for 100-70-03 and 120-90-02; and as-cast for 65-45-12 and 80-55-06. Castings shall be tested and conform to specified tensile requirements such as tensile strength, yield strength, and elongation. When indicated in the contract or purchase order, castings shall also adhere to special requirements like hardness, chemical composition, microstructure, pressure tightness, radiographic soundness, magnetic particle inspection dimensions, and surface finish.
Keywords:
casting, ductile iron, nodular iron, spheroidal graphite,, ICS Number Code 77.140.80 (Iron and steel castings)
Doplňujúce informácie
| 1. Scope | ||||||||||
|
1.1 This specification covers castings made of ductile iron, also known as spheroidal or nodular iron, which is described as cast iron with the graphite substantially spheroidal in shape and essentially free of other forms of graphite, as defined in Terminology A644. 1.2 No precise quantitative relationship can be stated between the properties of the iron in various locations of the same casting or between the properties of castings and those of a test specimen cast from the same iron (see Appendix X1). 1.3 The values stated in inch-pound units are to be regarded as standard. The values given in parentheses are mathematical conversions to SI units that are provided for information only and are not considered standard. 1.4 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee. |
||||||||||