ASTM A370-10
Standard Test Methods and Definitions for Mechanical Testing of Steel Products
Automaticky preložený názov:
Štandardné testovacie metódy a definície pre mechanické testovanie výrobkov z ocele
NORMA vydaná dňa 15.6.2010
Informácie o norme:
Označenie normy: ASTM A370-10
Poznámka: NEPLATNÁ
Dátum vydania normy: 15.6.2010
Kód tovaru: NS-2259
Počet strán: 47
Približná hmotnosť: 141 g (0.31 libier)
Krajina: Americká technická norma
Kategória: Technické normy ASTM
Anotácia textu normy ASTM A370-10 :
Keywords:
bend test, Brinell hardness, Charpy impact test, elongation, FATT (Fracture Appearance Transition Temperature), hardness test, portable hardness, reduction of area, Rockwell hardness, tensile strength, tension test, yield strength, Bend testing--metallic materials, Brinell hardness, Charpy impact test, Elongation--metallic materials, Forgings, Fracture appearance transition temperature (FATT), Generator materials, Hardness (indentation)--metallic materials, Impact resistance
Doplňujúce informácie
| Significance and Use | ||||||||||||||||||||||||||||||||||||||||
|
Ductile vs. Brittle Behavior—Body-centered-cubic or ferritic alloys exhibit a significant transition in behavior when impact tested over a range of temperatures. At temperatures above transition, impact specimens fracture by a ductile (usually microvoid coalescence) mechanism, absorbing relatively large amounts of energy. At lower temperatures, they fracture in a brittle (usually cleavage) manner absorbing appreciably less energy. Within the transition range, the fracture will generally be a mixture of areas of ductile fracture and brittle fracture. The temperature range of the transition from one type of behavior to the other varies according to the material being tested. This transition behavior may be defined in various ways for specification purposes. The specification may require a minimum test result for absorbed energy, fracture appearance, lateral expansion, or a combination thereof, at a specified test temperature. The specification may require the determination of the transition temperature at which either the absorbed energy or fracture appearance attains a specified level when testing is performed over a range of temperatures. Alternatively the specification may require the determination of the fracture appearance transition temperature (FATTn) as the temperature at which the required minimum percentage of shear fracture (n) is obtained. Further information on the significance of impact testing appears in Annex A5. |
||||||||||||||||||||||||||||||||||||||||
| 1. Scope | ||||||||||||||||||||||||||||||||||||||||
|
1.1 These test methods cover procedures and definitions for the mechanical testing of steels, stainless steels, and related alloys. The various mechanical tests herein described are used to determine properties required in the product specifications. Variations in testing methods are to be avoided, and standard methods of testing are to be followed to obtain reproducible and comparable results. In those cases in which the testing requirements for certain products are unique or at variance with these general procedures, the product specification testing requirements shall control. |
||||||||||||||||||||||||||||||||||||||||