Standard Specification for Gray Iron Castings for Elevated Temperatures for Non-Pressure Containing Parts
Automaticky preložený názov:
Štandardné špecifikácie pre odliatky zo šedej liatiny pre zvýšené teploty na Non-Tlakové obsahujúce diely
NORMA vydaná dňa 1.3.2011
Označenie normy: ASTM A319-71(2011)
Poznámka: NEPLATNÁ
Dátum vydania normy: 1.3.2011
Kód tovaru: NS-2012
Počet strán: 2
Približná hmotnosť: 6 g (0.01 libier)
Krajina: Americká technická norma
Kategória: Technické normy ASTM
Keywords:
chemical composition, elevated temperature, gray iron, iron castings, non-pressure containing, tensile strength: Grate bars, Gray iron castings--specifications, Ingot molds, Metal melting pots, Oil still furnace parts, Stoker links, Caustic pots, Elevated temperature service applications, Firebox parts, Glass molds, ICS Number Code 77.140.80 (Iron and steel castings)
1. Scope | ||
1.1 This specification covers three classes of gray iron suitable for castings exposed to temperatures encountered in such service as grate bars, stoker links, stoker parts, oil still furnace parts, firebox parts, ingot molds, glass molds, caustic pots, and metal melting pots. Note 1—This specification is general, covering cast irons normally used for the above types of service, at temperatures as high as 1400°F (760°C). It is not intended to imply that all three classes are suitable throughout this entire temperature range without regard to actual service stresses. Some are suitable for long service at the lower temperatures only, unless low stresses are involved. 1.2 The three classes of gray iron covered by this specification are as follows: 1.2.1 Class I, possessing superior resistance to thermal shock, 1.2.2 Class II, possessing average resistance to thermal shock and a moderately good tensile strength (tensile strengths above 30 000 psi (207 MPa) may be expected), and 1.2.3 Class III, possessing a higher tensile strength than either Classes I or II (tensile strengths as high as 40 000 psi (276 MPa) may be expected). 1.3 The values stated in inch-pound units are to be regarded as standard. The values given in parentheses are mathematical conversions to SI units that are provided for information only and are not considered standard. |
||
2. Referenced Documents | ||
|
Chcete mať istotu, že používate len platné technické normy?
Ponúkame Vám riešenie, ktoré Vám zaistí mesačný prehľad o aktuálnosti noriem, ktoré používate.
Chcete vedieť viac informácií ? Pozrite sa na túto stránku.
Posledná aktualizácia: 2024-11-22 (Počet položiek: 2 206 568)
© Copyright 2024 NORMSERVIS s.r.o.