ASTM A1066/A1066M-11(2015)e1
Standard Specification for High-Strength Low-Alloy Structural Steel Plate Produced by Thermo-Mechanical Controlled Process (TMCP) (Includes all amendments And changes 11/30/2017).
Automaticky preložený názov:
Štandardné špecifikácie pre vysoko pevných Low - Alloy konštrukčná oceľ Plate Produkoval Thermo - Mechanical riadený proces ( TMCP )
NORMA vydaná dňa 1.9.2015
Informácie o norme:
Označenie normy: ASTM A1066/A1066M-11(2015)e1
Poznámka: NEPLATNÁ
Dátum vydania normy: 1.9.2015
Kód tovaru: NS-615679
Počet strán: 4
Približná hmotnosť: 12 g (0.03 libier)
Krajina: Americká technická norma
Kategória: Technické normy ASTM
Kategórie - podobné normy:
Anotácia textu normy ASTM A1066/A1066M-11(2015)e1 :
Keywords:
steel plates, high-strength low-alloy steel, thermo-mechanical controlled rolling, structural steel, welded construction,, ICS Number Code 77.140.50 (Flat steel products and semi-products)
Doplňujúce informácie
| 1. Scope | ||||
|
1.1 This specification covers steel plates produced by the thermo-mechanical controlled process (TMCP). Five grades are defined by the yield strength: 50 [345], 60 [415], 65 [450], 70 [485], and 80 [550]. The plates are intended primarily for use in welded steel structures. 1.2 The TMCP method consists of rolling reductions and cooling rate controls that result in mechanical properties in the finished plate that are equivalent to those attained using conventional rolling and heat treatment processes, which entail reheating after rolling. A description of the TMCP method is given in Appendix X1. 1.3 The maximum thicknesses available in the grades covered by this specification are shown in Table 1. 1.4 Due to the special combination of
mechanical and thermal treatment inducing lower rolling
temperatures than for conventional hot rolling the plates can not
be formed at elevated temperatures without sustaining significant
losses in strength and toughness. The plates may be formed and
post-weld heat-treated at temperatures not exceeding 1050°F
[560°C]. Higher temperatures may be possible if proven that minimum
mechanical characteristics are retained after tests with specimens
in the post-weld heat treatment (PWHT) condition. For flame
straightening higher temperatures can be used in accordance with
the steel manufacturer’s recommendations.
1.5 If the steel is to be welded, a welding procedure suitable for the grade of steel and intended use or service is to be utilized. See Appendix X3 of Specification A6/A6M for information on weldability. 1.6 Supplementary requirements are available but shall apply only if specified in the purchase order. 1.7 The values stated in either inch-pound-units or SI units are to be regarded separately as standard. Within the text, the SI units are shown in brackets. The values stated in each system are not exact equivalents; therefore, each system is to be used independently of the other, without combining values in any way. |
||||