Standard Specification for Aluminum-Alloy Permanent Mold Castings
NORMA vydaná dňa 1.9.2019
Prečo Redline?
Redline predstavuje rýchly a jednoduchý spôsob ako porovnať všetky zmeny medzi aktuálne platnou normou a predchádzajúcou verziou.
Vďaka redline sa okamžite dozviete o:
Ušetrite si čas aj starosti!
Vďaka Redline už nebudete musieť strácať čas zisťovaním, čo sa v novej norme zmenilo. Redline Vám ušetrí čas a zaručí, že sa o zmenách v norme dozviete.
Cena
Ak si zvolíte možnosť "Platná norma + Redline", potom dostanete oba dokumenty! A čo je najlepšie, cena Platné normy + Redline je len o niečo málo vyššia ako cena samostatnej platné normy.
Označenie normy: ASTM B108/B108M-19
Dátum vydania normy: 1.9.2019
Počet strán: 23
Približná hmotnosť: 69 g (0.15 libier)
Krajina: Americká technická norma
Kategória: Technické normy ASTM
This specification covers aluminum-alloy permanent mold castings. The responsibility of furnishing castings that can be laid out and machined to the finished dimensions within the permissible variations specified shall rest with the producer, except where mold equipment is furnished by the purchaser. Samples for chemical analysis shall be taken by sawing, drilling, or milling the casting or test specimens in such a manner as to be representative of the material. Unless otherwise specified, only aluminum or producers foundry scrap shall be used in the re-melting furnace from which molten metal is taken for pouring directly into castings. Pure materials, recycled materials, and master alloys may be used to make alloys conforming to this specification. Foundry control shall consist of examination of castings by radiographic or other approved methods for determining internal discontinuities until the gating, pouring, and other foundry practices have been established to produce castings meeting the quality standards furnished by the purchaser or agreed upon by the purchaser and the producer. Separately cast test specimens shall be cast in iron molds. If the castings are to be heat treated and separately cast specimens are to be used, the specimens representing such castings shall be heat treated with the castings they represent. If castings are to be heat treated and tests are to be obtained on the castings, the test specimens shall be taken from the castings after heat treatment. One per melt-heat combination shall be tested when tensile properties of castings are to be determined. The finished castings shall be uniform in composition and free of blowholes, cracks, shrinks, and other discontinuities.
Keywords:
aluminum, permanent mold castings,, ICS Number Code 77.150.10 (Aluminium products)