ASTM B565-04(2015)
Standard Test Method for Shear Testing of Aluminum and Aluminum-Alloy Rivets and Cold-Heading Wire and Rods
Automaticky preložený názov:
Štandardná testovacia metóda pre šmykové testovania hliníka a hliníkových zliatin nity a studena Okruh drôty a prúty
NORMA vydaná dňa 1.10.2015
Informácie o norme:
Označenie normy: ASTM B565-04(2015)
Poznámka: NEPLATNÁ
Dátum vydania normy: 1.10.2015
Kód tovaru: NS-616739
Počet strán: 3
Približná hmotnosť: 9 g (0.02 libier)
Krajina: Americká technická norma
Kategória: Technické normy ASTM
Kategórie - podobné normy:
Anotácia textu normy ASTM B565-04(2015) :
Keywords:
double shear loading, shear test device, shear aluminum rivet ,, ICS Number Code 77.150.30 (Copper products)
Doplňujúce informácie
| Significance and Use | ||
|
5.1 This test method is intended solely for the shear testing of rivets and cold-heading wire and rod, and is not generally recommended for the determination of the shear strength of other products. For rivets, this method is limited to rivets having a shank length equal to or greater than 2d. Note 2: The results of shear tests of specimens machined from
products other than wire, rod, and rivets may be greatly dependent
upon the orientation of the specimen within the original test
material, and the direction in which the force is applied relative
to the grain flow in the specimen.4 It
is recommended that shear strengths of other products be determined
by Test Method B769 for
products greater than 0.250 in. (6.4 mm) and Test Method
B831 for products less than
0.250 in. (6.4 mm). Shear strengths developed by this test method
have been shown to vary from those developed by other
methods.5.2 The results of shear tests are
dependent upon the relative and absolute lengths of specimen which
are sheared out, and those which are supported.4
The results of tests made in accordance with this method should not
be directly compared with those determined in other types of tests
in which the methods of loading and supporting the specimen are
different.
5.3 The presence of a lubricant on the surfaces of the specimen and device may result in shear strengths up to 3 % lower than those determined in the absence of lubrication. Note 3: In order to be able to test rivets having shanks as
short as 2
|
d = nominal diameter of specimen (rivet, wire, or machined specimen), | |
| d1 = actual diameter of hole (see Note), and | ||
| d2 = actual diameter of specimen | ||
| Clearance (d1− d2), maximum = 0.02 d + 0.005 in. (0.12 mm) | ||
|
Note 1: The tolerance applicable to the diameter of the
specimen being shear tested must be recognized in drilling the hole
in the device. It is recommended that the drilled hole size be
equal to 1.02
|
S1 = d | |
| S2 = S1 + 0.001 in. (0.025 mm) | ||
| S3 = 1/4 in. (6 mm) for d = 1/16 in. (1.5 mm) to 5/32 in. (4 mm) | ||
| = 1/2 in. (12 mm) for d = 3/16 in. (5 mm) to 3/8 in. (10 mm) |
5.4 Investigations have determined that the shear strength decreases slightly as the clearance between the specimen diameter and the diameter of the test hole in the device increases, and that the effect of the clearance decreases with increasing specimen diameter. This test method (refer to Fig. 1) permits clearances for production testing which should affect shear strengths by no more than 2 %. For referee testing, the maximum clearance shall be 0.001 in. (0.03 mm).1.1 This test method covers the double shear testing of aluminum and aluminum alloy rivets with round, solid shanks and cold-heading wire and rod.2
Note 1: Exceptions to this test method may be necessary in
individual specifications or methods for tests for a particular
material.
1.2 The values stated in inch-pound units are to be regarded as standard. The values given in parentheses are mathematical conversions to SI units that are provided for information only and are not considered standard.
1.3 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety and health practices and determine the applicability of regulatory limitations prior to use.
|
Standard Specification for Aluminum and Aluminum-Alloy Rivet and Cold-Heading Wire and Rods |
|
|
Standard Test Method for Shear Testing of Aluminum Alloys |
|
|
Standard Test Method for Shear Testing of Thin Aluminum Alloy Products |
|
|
Standard Practices for Force Calibration and Verification of Testing Machines |
|
|
Standard Terminology Relating to Methods of Mechanical Testing (Includes all amendments and changes 3/29/2023). |
Doporučujeme: